Suzhou preferred lithium copper foil processing
Galvanizing barrier layer: After the rough surface is galvanized, a barrier layer is formed to improve the oxidation resistance of the copper foil in natural air. After galvanizing, the appearance will look gray. After a period of storage, the gray will turn into copper yellow. The more zinc is plated, the more yellow the copper foil will be.
Suzhou preferred lithium copper foil processing
The electrolyte contains oil, paint, grease, sediment and other contaminants attached to the surface of copper foil. After being squeezed by the squeezing (water) roller, the contaminants are squeezed flat, some contaminants attach to it, and some contaminants attach to the guide roller. Because the dirt is squeezed up during the operation, the dirt has a head and a tail, and has a direction.
Suzhou preferred lithium copper foil processing
Curing treatment: deposit a layer of dense metal copper in the nodular particle gap of the roughening layer, increase the contact surface between the roughening layer and the wool foil substrate, and reduce the roughness of the roughening layer surface. Microscopically, after rough surface roughening treatment, the foil surface is uneven and undulating greatly, while after curing treatment, the copper foil surface is relatively flat. After curing treatment, although the roughness is reduced, the bonding strength between the treatment layer and the insulating substrate material is improved due to the increased contact area between the roughened layer and the wool foil, which fundamentally eliminates the delamination between the treatment layer and the wool foil.
Suzhou preferred lithium copper foil processing
Copper foil can be divided into many kinds according to different classifications. According to the thickness, it can be divided into: thickness (more than 70 μ m) Regular thickness copper foil (more than 18 μ M but less than 70 μ m) Thin copper foil (more than 12 μ M but less than 18 μ m) Ultra thin copper foil (less than 12 μ m) Etc.
Suzhou preferred lithium copper foil processing
Silane coupling agent treatment: after anti oxidation treatment, the surface is sprayed with silane, which can improve the oxidation resistance at room temperature on the one hand; On the other hand, in high temperature pressing plate, silane can better combine copper foil and resin substrate through coupling, and improve peel strength. Post treatment process - drying. In order to prevent the harm of residual moisture, it must be dried at not less than 100 ℃ later, and the drying temperature cannot be too high.
Suzhou preferred lithium copper foil processing
Calendered copper foil is the original foil made from copper plate by repeated rolling, and then roughened according to requirements. Due to the limitation of processing technology, its width is difficult to meet the requirements of rigid copper clad laminate, so calendered copper foil is rarely used on rigid copper clad laminate; However, because the bending resistance and elastic coefficient are greater than electrolytic copper foil, they are often used on flexible copper clad laminate.