With electrolytic copper or wire return material of equal purity as raw material, it is dissolved in the solution containing copper sulfate. Electrolysis is carried out in an electrolytic cell with insoluble material as anode and cathode roller immersed in copper sulfate electrolyte at constant speed as cathode. Copper in the solution is deposited on the surface of cathode roller to form copper foil. The thickness is controlled by cathode current density and cathode roller speed. After the roller rotates out of the liquid level, it is continuously stripped from the cathode roll, washed, dried and rolled to generate the original foil.
Maoming preferred copper foil processing
Small dirt, small exclamation mark. During the production of raw foil, the hair side is upward, and the dirt in liquid and air all fall on the hair side, which is printed on the smooth side after rolling. The reason is that the stains on the cathode roll are not dried. The surface temperature of the cathode roll is only 50 degrees, and the air temperature in the workshop is generally about 25 degrees. The surface hairiness is very good. The dirt itself has water, and the drying time is only 2-3 minutes. Therefore, the dirt on the copper foil cannot be completely dried.
Maoming preferred copper foil processing
The production process of electrolytic copper foil is simple. There are three main processes: solution raw foil, surface treatment and product slitting. The production process seems simple, but it is a production process that integrates electronics, machinery and electrochemistry, and is particularly strict with the production environment. Therefore, the industry does not have a set of standard and universal production equipment and technology, and each manufacturer shows its own ingenuity, which is also an important bottleneck affecting the improvement of domestic production capacity and quality. In addition, the different requirements of customers have also resulted in the waste of many intermediate products copper foil in manufacturing. The one-time input-output ratio is even less than 80%, and these copper foils have to be manufactured again, wasting resources.
Maoming preferred copper foil processing
Electrolytic copper foil is made by dissolving copper into copper sulfate solution, electrodepositing the copper sulfate electrolyte under the action of direct current in special electrolytic equipment to make the original foil, and then carrying out surface treatment, heat-resistant layer treatment, oxidation prevention treatment and other surface treatment processes on the original foil according to customer requirements.
Maoming preferred copper foil processing
Although the thickness of copper foil gradually becomes thinner, power battery manufacturers use 6 μ When the product is less than or equal to m, the coating machine, winding machine and other key equipment as well as the technological level cannot solve the problems such as wrinkles, belt breakage and high-temperature oxidation encountered in the production process, which leads to the inability to mass produce ultra-thin copper foil with high yield.
Maoming preferred copper foil processing
Galvanizing barrier layer: After the rough surface is galvanized, a barrier layer is formed to improve the oxidation resistance of the copper foil in natural air. After galvanizing, the appearance will look gray. After a period of storage, the gray will turn into copper yellow. The more zinc is plated, the more yellow the copper foil will be.