Shantou Select Ultra thin Copper Foil Manufacturer
Silane coupling agent treatment: after anti oxidation treatment, the surface is sprayed with silane, which can improve the oxidation resistance at room temperature on the one hand; On the other hand, in high temperature pressing plate, silane can better combine copper foil and resin substrate through coupling, and improve peel strength. Post treatment process - drying. In order to prevent the harm of residual moisture, it must be dried at not less than 100 ℃ later, and the drying temperature cannot be too high.
Shantou Select Ultra thin Copper Foil Manufacturer
Although the thickness of copper foil gradually becomes thinner, power battery manufacturers use 6 μ When the product is less than or equal to m, the coating machine, winding machine and other key equipment as well as the technological level cannot solve the problems such as wrinkles, belt breakage and high-temperature oxidation encountered in the production process, which leads to the inability to mass produce ultra-thin copper foil with high yield.
Shantou Select Ultra thin Copper Foil Manufacturer
With electrolytic copper or wire return material of equal purity as raw material, it is dissolved in the solution containing copper sulfate. Electrolysis is carried out in an electrolytic cell with insoluble material as anode and cathode roller immersed in copper sulfate electrolyte at constant speed as cathode. Copper in the solution is deposited on the surface of cathode roller to form copper foil. The thickness is controlled by cathode current density and cathode roller speed. After the roller rotates out of the liquid level, it is continuously stripped from the cathode roll, washed, dried and rolled to generate the original foil.
Shantou Select Ultra thin Copper Foil Manufacturer
Foil making material requirements: the thinner the thickness is, the higher the quality grade is, and the lower the impurity content in the electrolyte is required. In order to ensure the quality, the purity of copper must be greater than 99.9%.
Shantou Select Ultra thin Copper Foil Manufacturer
The surface of the copper foil shall be smooth and clean without obvious wrinkles, oxidation spots, scratches, pitting, pits and stains. The porosity of 305g/m2 and above shall not exceed 8 penetration points within the area of 300ram × 300mm; The total area of pores on an area of 0.5m2 shall not exceed the circular area with a diameter of 0.125mm.
Shantou Select Ultra thin Copper Foil Manufacturer
If the rough surface and pinholes appear at the same time when there are stains on the rough surface, it indicates that the stains are caused by the dirty electrolyte, and the dirt is attached to the copper foil in the electrolytic cell. If there are stains on the rough surface, the copper foil is not rough and there are no pinholes, it means that the workshop production environment is dirty, the air contains dust, or other suspended impurities fall on the surface of the copper foil.