Zhanjiang Preferred Copper Foil Processing
Backward key production equipment: for high-quality products with production thickness less than 0.05mm, multi roll rolling mill with width meeting user requirements shall be used. The rolling mill of some domestic copper processing plants can not be normally put into rolling foil production due to the lack of other equipment or the traditional product structure in the factory. However, some small processing plants have to use outdated production equipment and processes due to lack of key equipment or investment capacity, and copper foil product specifications and technical indicators are inferior to foreign products.
Zhanjiang Preferred Copper Foil Processing
The copper foil industry belongs to the copper processing industry, which processes copper into extremely thin copper strips or sheets by means of rolling, electrolysis and sputtering, and further applies them as industrial raw materials in various downstream products. The thickness of μ Below m, the thickness varies depending on the scene used.
Zhanjiang Preferred Copper Foil Processing
Curing treatment: deposit a layer of dense metal copper in the nodular particle gap of the roughening layer, increase the contact surface between the roughening layer and the wool foil substrate, and reduce the roughness of the roughening layer surface. Microscopically, after rough surface roughening treatment, the foil surface is uneven and undulating greatly, while after curing treatment, the copper foil surface is relatively flat. After curing treatment, although the roughness is reduced, the bonding strength between the treatment layer and the insulating substrate material is improved due to the increased contact area between the roughened layer and the wool foil, which fundamentally eliminates the delamination between the treatment layer and the wool foil.
Zhanjiang Preferred Copper Foil Processing
The calendered copper foil is made by repeated rolling annealing process of copper ingot based on the principle of plastic processing. Its internal structure is lamellar crystal structure, and the product has good ductility. At present, it is mainly used in the production of rigid circuit boards, while the rolled copper foil is mainly used in flexible and high-frequency circuit boards.
Zhanjiang Preferred Copper Foil Processing
Surface passivation: chromate (or chromate and zinc salt) solution is used for surface passivation (i.e. anti oxidation treatment) after the barrier layer is plated to form a complex film with chromium (or chromium zinc) as the main body on the surface, so that the copper foil will not be oxidized and discolored due to direct contact with air, and at the same time, the heat resistance of the copper foil is improved (higher zinc content, better heat resistance), The storage period of copper foil can reach 3 months.
Zhanjiang Preferred Copper Foil Processing
The adhesives used for the laminates mainly include phenolic, epoxy, polyester, polyimide, polytetrafluoroethylene resin, etc. Therefore, the laminates are also divided into phenolic, epoxy, polyester, polyimide, and polytetrafluoroethylene laminates.