Dongguan Preferred Battery Copper Foil Manufacturer
The production process of electrolytic copper foil is simple. There are three main processes: solution raw foil, surface treatment and product slitting. The production process seems simple, but it is a production process that integrates electronics, machinery and electrochemistry, and is particularly strict with the production environment. Therefore, the industry does not have a set of standard and universal production equipment and technology, and each manufacturer shows its own ingenuity, which is also an important bottleneck affecting the improvement of domestic production capacity and quality.
Dongguan Preferred Battery Copper Foil Manufacturer
Excellent tensile strength and elongation High tensile strength and elongation under normal conditions can improve processing ability, enhance rigidity and avoid wrinkles to improve production qualification rate. High temperature extensibility (THE) copper foil and high tensile strength copper foil at high temperature can improve the thermal stability of printed boards and avoid deformation and warpage.
Dongguan Preferred Battery Copper Foil Manufacturer
With the development of high-density wiring technology for low profile copper foil multilayer boards, the traditional type cannot meet the needs of manufacturing high-precision printed circuit boards. Therefore, a new generation of copper foils, low profile (LP) and ultra-low profile (VLP), have emerged one after another. Compared with ordinary electrolytic copper foil, LP copper foil has fine crystal (2/zm), equiaxed grains, no columnar crystals, lamellar crystals, flat prisms and low surface roughness.
Dongguan Preferred Battery Copper Foil Manufacturer
Silane coupling agent treatment: after anti oxidation treatment, the surface is sprayed with silane, which can improve the oxidation resistance at room temperature on the one hand; On the other hand, in high temperature pressing plate, silane can better combine copper foil and resin substrate through coupling, and improve peel strength. Post treatment process - drying. In order to prevent the harm of residual moisture, it must be dried at not less than 100 ℃ later, and the drying temperature cannot be too high.
Dongguan Preferred Battery Copper Foil Manufacturer
Curing treatment: deposit a layer of dense metal copper in the nodular particle gap of the roughening layer, increase the contact surface between the roughening layer and the wool foil substrate, and reduce the roughness of the roughening layer surface. Microscopically, after rough surface roughening treatment, the foil surface is uneven and undulating greatly, while after curing treatment, the copper foil surface is relatively flat. After curing treatment, although the roughness is reduced, the bonding strength between the treatment layer and the insulating substrate material is improved due to the increased contact area between the roughened layer and the wool foil, which fundamentally eliminates the delamination between the treatment layer and the wool foil.