Suzhou Preferred Copper Foil Processing
Copper foil is an indispensable raw material for making printed circuit board (PCB), copper clad plate (CCL) and lithium-ion battery. For industrial use, it can be divided into calendered copper foil and two categories according to its manufacturing process. Electrolytic copper foil is made by electrolysis of copper based on electrochemical principle. The internal structure of raw foil is vertical acicular crystal structure, and its production cost is relatively low.
Suzhou Preferred Copper Foil Processing
If the rough surface and pinholes appear at the same time when there are stains on the rough surface, it indicates that the stains are caused by the dirty electrolyte, and the dirt is attached to the copper foil in the electrolytic cell. If there are stains on the rough surface, the copper foil is not rough and there are no pinholes, it means that the workshop production environment is dirty, the air contains dust, or other suspended impurities fall on the surface of the copper foil.
Suzhou Preferred Copper Foil Processing
Curing treatment: deposit a layer of dense metal copper in the nodular particle gap of the roughening layer, increase the contact surface between the roughening layer and the wool foil substrate, and reduce the roughness of the roughening layer surface. Microscopically, after rough surface roughening treatment, the foil surface is uneven and undulating greatly, while after curing treatment, the copper foil surface is relatively flat. After curing treatment, although the roughness is reduced, the bonding strength between the treatment layer and the insulating substrate material is improved due to the increased contact area between the roughened layer and the wool foil, which fundamentally eliminates the delamination between the treatment layer and the wool foil.
Suzhou Preferred Copper Foil Processing
Small dirt, small exclamation mark. During the production of raw foil, the hair side is upward, and the dirt in liquid and air all fall on the hair side, which is printed on the smooth side after rolling. The reason is that the stains on the cathode roll are not dried. The surface temperature of the cathode roll is only 50 degrees, and the air temperature in the workshop is generally about 25 degrees. The surface hairiness is very good. The dirt itself has water, and the drying time is only 2-3 minutes. Therefore, the dirt on the copper foil cannot be completely dried.