Silane coupling agent treatment: after anti oxidation treatment, the surface is sprayed with silane, which can improve the oxidation resistance at room temperature on the one hand; On the other hand, in high temperature pressing plate, silane can better combine copper foil and resin substrate through coupling, and improve peel strength. Post treatment process - drying. In order to prevent the harm of residual moisture, it must be dried at not less than 100 ℃ later, and the drying temperature cannot be too high.
Tongling Preferred Electronic Copper Foil Manufacturer
The ultra-thin copper foil, represented by mobile phones and laptops, is promoted to thin foil and ultra-thin foil types for portable electronic products, including micro buried, blind hole L multilayer boards, and BGA, CSP and other organic resin packaging substrates. At the same time, COz laser etching also requires the substrate to be extremely thin, so that the copper foil layer can be directly machined with micro wire holes. In Japan, the United States and other countries, electrolytic copper foils of 9 μ m, 5 μ m and 3/- tm can be industrialized. At present, the difficulty or key point of the production technology of ultra-thin copper foil is whether it can be directly produced without carrier, and the product qualification rate is high, as well as the development of new carriers.
Tongling Preferred Electronic Copper Foil Manufacturer
The commonly used reinforcement materials of copper clad laminate are alkali free (alkali metal oxide content shall not exceed 0.5%) glass fiber products (such as glass cloth, glass felt) or paper (such as wood pulp paper, bleached wood pulp paper, cotton wool paper). Therefore, laminates can be divided into glass cloth base and paper base.
Tongling Preferred Electronic Copper Foil Manufacturer
Galvanizing barrier layer: After the rough surface is galvanized, a barrier layer is formed to improve the oxidation resistance of the copper foil in natural air. After galvanizing, the appearance will look gray. After a period of storage, the gray will turn into copper yellow. The more zinc is plated, the more yellow the copper foil will be.
Tongling Preferred Electronic Copper Foil Manufacturer
Electrolytic copper foil is made by dissolving copper into copper sulfate solution, electrodepositing the copper sulfate electrolyte under the action of direct current in special electrolytic equipment to make the original foil, and then carrying out surface treatment, heat-resistant layer treatment, oxidation prevention treatment and other surface treatment processes on the original foil according to customer requirements.
Tongling Preferred Electronic Copper Foil Manufacturer
The copper clad laminate is composed of copper foil, reinforcement material and adhesive. Plates are usually classified according to the reinforcement material category and adhesive category or plate characteristics.