Huizhou Preferred Circuit Board Copper Foil Processing
Surface passivation: chromate (or chromate and zinc salt) solution is used for surface passivation (i.e. anti oxidation treatment) after the barrier layer is plated to form a complex film with chromium (or chromium zinc) as the main body on the surface, so that the copper foil will not be oxidized and discolored due to direct contact with air, and at the same time, the heat resistance of the copper foil is improved (higher zinc content, better heat resistance), The storage period of copper foil can reach 3 months.
Huizhou Preferred Circuit Board Copper Foil Processing
Small dirt, small exclamation mark. During the production of raw foil, the hair side is upward, and the dirt in liquid and air all fall on the hair side, which is printed on the smooth side after rolling. The reason is that the stains on the cathode roll are not dried. The surface temperature of the cathode roll is only 50 degrees, and the air temperature in the workshop is generally about 25 degrees. The surface hairiness is very good. The dirt itself has water, and the drying time is only 2-3 minutes. Therefore, the dirt on the copper foil cannot be completely dried.
Huizhou Preferred Circuit Board Copper Foil Processing
The production process of electrolytic copper foil is simple. There are three main processes: solution raw foil, surface treatment and product slitting. The production process seems simple, but it is a production process that integrates electronics, machinery and electrochemistry, and is particularly strict with the production environment. Therefore, the industry does not have a set of standard and universal production equipment and technology, and each manufacturer shows its own ingenuity, which is also an important bottleneck affecting the improvement of domestic production capacity and quality.
Huizhou Preferred Circuit Board Copper Foil Processing
At the same time of thinning, it is also necessary to improve the tensile strength, elongation and other indicators, otherwise it is easy to cause copper foil fracture, affecting the safety of the battery. Therefore, it is the general trend that the future use will be more light and meet the above indicators.