Backward key production equipment: for high-quality products with production thickness less than 0.05mm, multi roll rolling mill with width meeting user requirements shall be used. The rolling mill of some domestic copper processing plants can not be normally put into rolling foil production due to the lack of other equipment or the traditional product structure in the factory. However, some small processing plants have to use outdated production equipment and processes due to lack of key equipment or investment capacity, and copper foil product specifications and technical indicators are inferior to foreign products.
Zhongshan chooses electrolytic copper foil processing
Galvanizing barrier layer: After the rough surface is galvanized, a barrier layer is formed to improve the oxidation resistance of the copper foil in natural air. After galvanizing, the appearance will look gray. After a period of storage, the gray will turn into copper yellow. The more zinc is plated, the more yellow the copper foil will be.
Zhongshan chooses electrolytic copper foil processing
Copper foil is not a traditional metal copper product. It combines design concepts such as composite material and nano material technology, and different internal microstructures, resulting in different properties from traditional pure copper. The application of copper foil mainly focuses on the characteristics of conduction, heat conduction and electromagnetic wave shielding.
Zhongshan chooses electrolytic copper foil processing
Silane coupling agent treatment: after anti oxidation treatment, the surface is sprayed with silane, which can improve the oxidation resistance at room temperature on the one hand; On the other hand, in high temperature pressing plate, silane can better combine copper foil and resin substrate through coupling, and improve peel strength. Post treatment process - drying. In order to prevent the harm of residual moisture, it must be dried at not less than 100 ℃ later, and the drying temperature cannot be too high.
Zhongshan chooses electrolytic copper foil processing
The calendered copper foil is made by repeated rolling annealing process of copper ingot based on the principle of plastic processing. Its internal structure is lamellar crystal structure, and the product has good ductility. At present, it is mainly used in the production of rigid circuit boards, while the rolled copper foil is mainly used in flexible and high-frequency circuit boards.
Zhongshan chooses electrolytic copper foil processing
The surface of the copper foil shall be smooth and clean without obvious wrinkles, oxidation spots, scratches, pitting, pits and stains. The porosity of 305g/m2 and above shall not exceed 8 penetration points within the area of 300ram × 300mm; The total area of pores on an area of 0.5m2 shall not exceed the circular area with a diameter of 0.125mm.