The surface of the copper foil shall be smooth and clean without obvious wrinkles, oxidation spots, scratches, pitting, pits and stains. The porosity of 305g/m2 and above shall not exceed 8 penetration points within the area of 300ram × 300mm; The total area of pores on an area of 0.5m2 shall not exceed the circular area with a diameter of 0.125mm.
Suzhou Preferred Rolling Copper Foil Manufacturer
During the production of copper foil, tiny foreign matters are adhered on the surface to form spots with different colors from the surface, which are called stains. Judgment method: use macroscopic inspection to judge whether it is a waste product, a secondary product or a finished product according to the number and area of stains and the impact on product quality.
Suzhou Preferred Rolling Copper Foil Manufacturer
In order to improve the bonding strength of copper foil to the substrate, oxidation is usually used (that is, after oxidation treatment, a layer of copper oxide or cuprous oxide is formed on the surface, which improves the bonding strength of copper foil and substrate due to the polarity) Or roughen the copper foil (a roughened layer is generated on the surface of the copper foil by electrochemical method, which increases the surface area of the copper foil and improves the bonding strength between the copper foil and the substrate due to the anchoring effect of the roughened layer on the substrate).
Suzhou Preferred Rolling Copper Foil Manufacturer
Silane coupling agent treatment: after anti oxidation treatment, the surface is sprayed with silane, which can improve the oxidation resistance at room temperature on the one hand; On the other hand, in high temperature pressing plate, silane can better combine copper foil and resin substrate through coupling, and improve peel strength. Post treatment process - drying. In order to prevent the harm of residual moisture, it must be dried at not less than 100 ℃ later, and the drying temperature cannot be too high.